2.4 Mm 1.6 Mm 1.5 Mm Annealed Stainless Steel Wire 19 Gauge 28 Gauge
Product Details:
Place of Origin: | Jiangsu, China |
Brand Name: | JIANGSU ZHIJIA STEEL |
Certification: | ISO9001, CE |
Payment & Shipping Terms:
Minimum Order Quantity: | Negotiation |
---|---|
Price: | Negotiation |
Delivery Time: | 7~10working days |
Payment Terms: | L/C, T/T |
Supply Ability: | 5000 Ton/Tons per Month |
Detail Information |
|||
Product Name: | Stainless Steel Sheet | Type: | Cold Rolled,Hot Rolled |
---|---|---|---|
Surface: | No.1,2D,2B,BA,No.4,8k,Tempered | Thickness: | 0.4mm~6mm |
High Light: | 1.5 mm stainless steel wire,1.6 mm stainless steel wire,2.4 mm stainless steel wire |
Product Description
Grade 304 Stainless Steel Sheet
304(1.4301)/304L(1.4307)/304H(1.4948) STAINLESS STEEL
Stainless Steel Grade 304 is the standard 18/8 (18% chrome, 8% nickel) austenitic stainless steel. It is a non-magnetic alloy in the annealed condition, however, becomes magnetic as it is cold worked. It is the most ordinarily utilized of all stainless grades. T304 can be effortlessly welded and is the preferred for many deep drawn, spun or formed parts due to its high ductility.
Stainless Steel Grade 304L has oxidation resistance to a maximum temperature of 1650°F (899°C) continuous without considerable scaling. The maximum temperature for intermittent presentation is 1500°F (816°C). Since 304L is an additional low-carbon variety of 304 it can frequently be utilized in the “as-welded” condition (without annealing), even in severe corrosive conditions, except for applications indicating stress relief. 304L has good welding qualities and can be welded by all standard strategy; however, consideration should be paid to maintain a strategic distance from weld “hot cracking”. To relieve stress during severe forming or spinning welding may be followed by annealing.
Stainless Steel Grade 304H includes a high carbon content making the steel more suitable for utilization in applications where high temperatures are available. The benefit of this grade is that it is an austenitic chromium-nickel steel alloy as well as the greater carbon content distribute to increased tensile and yield strength. The material is recommended for utilizing in ASME pressure vessels in working service above 525° C because of the grade's heat resistant properties.
CHEMICAL COMPOSITION
Element | C | Mn | Si | P | S | Cr | Ni | Fe |
302 | 0.15% | 2.0% | 0.75% | 0.045% | 0.03% | 17.0~19.0% | 8.0~10.0% | Remainder |
303 | 0.10% | 2.0% | 1.00% | 0.040% | 0.015% | 17.0~19.0% | 8.0~10.0% | Remainder |
304 | 0.07% | 2.0% | 0.75% | 0.045% | 0.03% | 17.5~19.5% | 8.0~10.5% | Remainder |
304L | 0.03% | 2.0% | 0.75% | 0.045% | 0.03% | 17.5~19.5% | 8.0~12.0% | Remainder |
304H | 0.04~0.10% | 2.0% | 0.75% | 0.045% | 0.03% | 18.0~20.0% | 8.0~10.5% | Remainder |
309 | 0.20% | 2.0% | 0.75% | 0.045% | 0.03% | 22.0~24.0% | 12.0~15.0% | Remainder |
321 | 0.08% | 2.0% | 0.75% | 0.045% | 0.03% | 17.0~19.0% | 9.0~12.0% | Remainder |
330 | 0.08% | 2.0% | 0.75~1.50% | 0.03% | 0.03% | 17.0~20.0% | 34.0~37.0% | Remainder |
347 | 0.08% | 2.0% | 0.75% | 0.045% | 0.03% | 17.0~19.0% | 9.0~13.0% | Remainder |
MECHANICAL PROPERTIES
Grade |
Tensile Strength (MPa) Min
|
Yield Strength 0.2% Proof (MPa) Min
|
Elongation (%in 50mm) Min |
Hardness | |
Rockwell B (HR B) Max |
Brinell (HB) Max |
||||
302 | 620 | 275 | 40 | 92 | 147 |
303 | 620 | 310 | 30 | 96 | 230 |
304 | 515 | 205 | 40 | 92 | 201 |
304L | 485 | 170 | 40 | 92 | 201 |
304H | 515 | 205 | 40 | 92 | 201 |
309 | 515 | 205 | 40 | 95 | 217 |
321 | 515 | 205 | 40 | 95 | 217 |
330 | 552 | 207 | 40 | 95 | 217 |
347 | 515 | 205 | 40 | 92 | 201 |
304/304L/304H COMMON APPLICATIONS
- Air Bag Sensors
- Clamps
- Bellows
- Flexible Hoses
- Hinges
- Cryogenic Components
- Surgical Instruments
- Pressure Vessels
- Oil Well Filter Screen
- Hypodermic Needles
- Medical Parts
- Tubing